| Abstract: | Investigations into the corrosion behaviour of stainless steels in phosphoric acid in dependence on the chloride and fluoride contents and a heat-treatment during welding In the present investigation the corrosion behaviour of recently developed high-alloyed austenitic (X 2 NiCrMoCU 25 20) and austenitic-ferritic (X 2 CrNiMoCuN 25 5) steel has been tested towards phosphoric acid, the composition and concentration of which was adjusted to correspond to crude phosphoric acid with varying contents of Cl?, F?, Fe3+, and SO3. Current density-voltage curves were recorded on steel test-specimens at room temperature, 45°C, and 80°C. In addition, test-pieces of both steels, after annealing treatment between 800°C and 500°C, as well as welded specimens of similar type were examined for the effect of heat input and consequent structural alterations on the corrosion behaviour. Both steels exhibit good corrosion resistance towards pure phosphoric acid. Cl? and F? ion impurities render the acid more aggressive. Austenitie-ferritic steel reacts more sensitively than austenitic steel towards heat input, resulting in deterioration in corrosion resistance. This may be attributed to the precipitation of inter-metallic phases in the ferritic structure. |