| Effects of rare earth elements on the microstructure and properties of magnesium alloy AZ91D |
| |
| 引用本文： | KaikunWang KuiZhang 等. Effects of rare earth elements on the microstructure and properties of magnesium alloy AZ91D[J]. 北京科技大学学报(英文版), 2002, 9(5): 363-366 |
| |
| 作者姓名： | KaikunWang KuiZhang 等 |
| |
| 作者单位： | [1]MaterialsScienceandEngineeringSchool,UniversityofScienceandTechnologyBeijing,Beijing100083,China [2]BeijingNonferrousMetalResarchInstitute,Beijing100088,China |
| |
| 基金项目： | 国家重点基础研究发展计划(973计划) |
| |
| 摘 要： | The effects of rare earth elements on the microstructure and properties of Magnesium alloy AZ91D alloy were studied.The different proportion of rare earth elements was added to the AZ91D and the tensile tests were carried out at different temperatures.The experimental results show that at room temperature or at 120℃ the AZ91D‘s decrease with the increasing amount of the rare earth elements.however,the ductility is improved.The influence of 0.14%Sb(mass fraction)on the AZ91D‘s strength is like that of rare earth elements(0.2%-0.4%)(mass fraction).Microstructure graphs demonstrate that appropriate amount of rare earth elements (0.1%-0.2%) can fine AZ91D‘s grain and improve its ductility.
|
| 关 键 词： | 镁合金 稀土元素 微结构 实验 |
Effects of rare earth elements on the microstructureand properties of magnesium alloy AZ91D |
| |
| Kaikun Wang,Yonglin Kang,Kui Zhang. Effects of rare earth elements on the microstructureand properties of magnesium alloy AZ91D[J]. Journal of University of Science and Technology Beijing, 2002, 9(5): 363-366 |
| |
| Authors: | Kaikun Wang Yonglin Kang Kui Zhang |
| |
| Abstract: | The effects of rare earth elements on the microstructure and properties of magnesium alloy AZ91D alloy were studied. The different proportion of rare earth elements was added to the AZ91D and the tensile tests were carried out at different temperatures. The experimental results show that at room temperature or at 120℃ the AZ91D's strength decrease with the increasing amount of the rare earth elements. However, the ductility is improved. The influence of 0.14%Sb (mass fraction) on the AZ91D's strength is like that of rare earth elements (0.2%-0.4%) (mass fraction). Microstructure graphs demonstrate that appropriate amount of rare earth elements (0.1%-0.2%) can fine AZ91D's grain and improve its ductility. |
| |
| Keywords: | magnesium alloy AZ91D rare earth elements strength ductility microstructure |