The effects of composition and γ′/γ lattice parameter mismatch on the critical resolved shear stresses for octahedral and cube slip in NiAlCrX alloys

Prototypical single-crystal NiAlCrX superalloys were studied to examine the effects of the common major alloying elements, Co, Mo, Nb, Ta, Ti, and W, on yielding behavior. The alloys contained about 10 at. pct Cr, 60 vol pct of the γ′ phase, and about 3 at. pct of X in the γ′. The critical resolved shear stresses (CRSSs) for octahedral and primary cube slip were measured at 760 °C, which is about the peak strength temperature. The CRSS_Oct and CRSS_cube are discussed in relation to those of Ni₃ (Al, X) γ′ alloys taken from the literature and the γ′/γ lattice mismatch. The CRSS_Oct of the γ+γ′ alloys reflected a similar compositional dependence to that of both the CRSS_Oct of the γ′ phase and the γ′/γ lattice parameter mismatch. The CRSS_cube of the γ+γ′ alloys also reflected the compositional dependence of the γ′/γ mismatch, but bore no similarity to that of CRSS_cube for γ′ alloys since it is controlled by the γ matrix. The ratio of CRSS_cube/CRSS_Oct was decreased by all alloying elements except Co, which increased the ratio. The decrease in CRSS_cube/CRSS_Oct was related to the degree in which elements partition to the γ′ rather than the γ phase.