STUDY ON HIGH TEMPERATURE DEFORMATION CHARACTERISTICS OF Cu–0.23%Al2O3 DISPERSION–STRENGTHENED COPPER ALLOY |
| |
Authors: | SHEN Kun WANG Mingpu GUO Mingxing LI Shumei |
| |
Affiliation: | 1) School of Materials Science and Engineering, Central South University, Changsha 4100832) Laboratory for Mechanical Metallurgy, Institut des Mat´eriaux, Ecole Polytechnique F´ed´erale de Lausanne (EPFL),Lausanne, Switzerland |
| |
Abstract: | In order to deeply understand the high temperature deformation behaviors of Cu–0.23%Al2O3 (volume fraction) alloy, the changes of flow stress and microstructure for this alloy after deformation at high temperatures were investigated by using the Gleeble–1500 hot simulator, metallographic microscope and transmission electron microscope. The results show that the flow stress will change significantly with the thermal compression conditions and is mainly divided into three different stages. In addition, the average activation energy and other material parameters of this alloy deformed at high temperatures were obtained, based on them, the constitutive equation of the peak value yield stress–strain rate–temperature was also established. With increasing of compression temperature, the size and number of dynamic recrystallization grains are increased. However in the case of isothermal compression, with increasing of strain rates, the evolution of metallographical microstructures becomes disequilibrium, the size of subgrain is gradually decreased to about 0.5—1 μm, and the dislocation density is increased at first, and then decreased. |
| |
Keywords: | 2O3 alloyzz')" href=" #" > Cu&ndash Al2O3 alloy high temperature deformation constitutive equation dynamic recovery dynamic recrystallization |
|
| 点击此处可从《金属学报》浏览原始摘要信息 |
|
点击此处可从《金属学报》下载全文 |
|