Effect of calcined colemanite additions on properties of hard porcelain body |
| |
Affiliation: | 1. School of Resources and Environmental Engineering, Wuhan University of Technology, Luoshi Road 122, Wuhan, Hubei, 430070, China;2. Instituto de Metalurgia, Universidad Autonoma de San Luis Potosi, Av. Sierra Leona 550, San Luis Potosi, C.P. 78210, Mexico;1. Department of Physics & Astrophysics, University of Delhi, Delhi 110007, India;2. National Physical Laboratory, Dr. K. S. Krishnan Marg, New Delhi 110012, India;3. University Science Instrumentation Center, Univ. of Delhi, Delhi 110007, India;1. Mathematical Institution, Fujian Jiangxia University, Fuzhou, Fujian 350108, China;2. Electronic Information Science Institution, Fujian Jiangxia University, Fuzhou, Fujian 350108, China;3. College of Mechanical and Electronic Engineering, Fujian Agriculture and Forestry University, Fuzhou, Fujian 350108, China |
| |
Abstract: | Utilization of calcined colemanite as a sintering aid in hard porcelain body, prepared by slip casting route using aqueous suspension containing mixtures of kaolin, quartz and potassium feldspar, was investigated. After calcination, colemanite powders were added to the admixture of porcelain by partial substitution with potassium feldspars in the range of 0–5 wt% to discover its influences on the densification and technological properties of the final product. Through optimization of process parameters of ceramic suspensions by using appropriate dispersing agents and facilitating densification by calcined colemanite addition, hard porcelain possess high strength was obtained. When relationship between the additive concentration with temperature was established, it is found that porcelain formulations resulted in substantial reduction of firing temperature about 50 °C without compromising its quality by 1 wt% calcined colemanite addition. |
| |
Keywords: | Porcelain Colemanite Microwave assisted calcination Firing temperature |
本文献已被 ScienceDirect 等数据库收录! |
|