Influence of Yb3+ doping on phase stability and thermophysical properties of (Y1-xYbx)3Al5O12 under high temperature

In this work, Yb³⁺ was selected to replace the Y³⁺ in yttrium aluminum garnet (YAG) in order to reduce its thermal conductivity under high temperature. A series of (Y_1-xYb_x)₃Al₅O₁₂ (x=0, 0.1, 0.2, 0.3, 0.4) ceramics were prepared by solid-state reaction at 1600 °C for 10 h. The microstructure, thermophysical properties and phase stability under high temperature were investigated. The results showed that all the Yb doped (Y_1-xYb_x)₃Al₅O₁₂ ceramics were comprised of a single garnet-type Y₃Al₅O₁₂ phase. The thermal conductivities of (Y_1-xYb_x)₃Al₅O₁₂ ceramics firstly decreased and subsequently increased with Yb ions concentration rising from room temperature to 1200 °C. (Y_0.7Yb_0.3)₃Al₅O₁₂ had the lowest thermal conductivity among investigated specimens, which was about 1.62 W m^?1 K^?1 at 1000 °C, around 30% lower than that of pure YAG (2.3 W m^?1 K^?1, 1000 °C). Yb had almost no effect on the coefficients of thermal expansion (CTEs) of (Y_1-xYb_x)₃Al₅O₁₂ ceramics and the CTE was approximate 10.7×10^?6 K^?1 at 1200 °C. In addition, (Y_0.7Yb_0.3)₃Al₅O₁₂ ceramic remained good phase stability when heating from room temperature to 1450 °C.