| 水热法制备超细球形氧化铝粉体 |
| |
| 引用本文： | 孙敬会,伊家飞,卿培林,张旭明,徐敬尧,周小丽. 水热法制备超细球形氧化铝粉体[J]. 中国陶瓷, 2021, 0(1): 30-35 |
| |
| 作者姓名： | 孙敬会 伊家飞 卿培林 张旭明 徐敬尧 周小丽 |
| |
| 作者单位： | 百色学院材料科学与工程学院 |
| |
| 基金项目： | 2020年度广西高校中青年教师科研基础能力提升项目(2020KY19020);2020年度广西高校中青年教师科研基础能力提升项目(2020KY19023);2019年度广西高校中青年教师科研基础能力提升项目(2019KY0757);广西壮族自治区硕士学位授予单位立项建设经费资助。 |
| |
| 摘 要： | 以较为经济的水合硫酸铝为铝源,尿素为沉淀剂,利用水热法在内胆为聚四氟乙烯的水热釜中制备氧化铝前驱体,然后将烘干后的前驱体进行高温煅烧,制得超细球形氧化铝粉体.重点探究了水热反应温度、反应时间对产物微观形貌及粒度的影响,并对氧化铝粉体煅烧前后的微观形貌进行了对比.实验结果表明:前驱体的形貌具有遗传性;在水热反应温度120...
|
| 关 键 词： | 水热法 高成球率 球形氧化铝 |
Preparation of Ultra-fine Spherical Aluminum Oxide Powder by Hydrothermal Method |
| |
| SUN Jinghui,YI Jiafei,QING Peilin,ZHANG Xuming,XU Jinyao,ZHOU Xiaoli. Preparation of Ultra-fine Spherical Aluminum Oxide Powder by Hydrothermal Method[J]. China Ceramics, 2021, 0(1): 30-35 |
| |
| Authors: | SUN Jinghui YI Jiafei QING Peilin ZHANG Xuming XU Jinyao ZHOU Xiaoli |
| |
| Affiliation: | (College of Materials Science and Engineering,Baise University,Baise 533000,China) |
| |
| Abstract: | In this study,alumina precursor was prepared by hydrothermal method in polytetrafluoroethylenelined hydrothermal autoclave using the economical aluminium sulphate hydrate as aluminium source and urea as precipitant.Ultrafine spherical alumina powder was prepared by calcining the dried precursor at high temperature.The effects of hydrothermal reaction temperature and reaction time on the micro-morphology and particle size of the product were mainly investigated,and the micro-morphology of alumina powder before and after calcination was compared.The results show that the morphology of the precursor is hereditary;when the hydrothermal reaction temperature is 120℃and the reaction time is 2 h,the calcination temperature is 1200℃and the calcination time is 2 h,the spherical alumina powder with 99.9%globular percentage,1.61μm average particle size and good dispersion is obtained. |
| |
| Keywords: | Hydrothermal method High globulan percentage Spherical alumina |