Combined pre-annealing and pre-oxidation treatment for the processing of thermal barrier coatings on NiCoCrAlY bond coatings

A combined pre-annealing and pre-oxidation treatment was developed for the processing of partially yttria stabilized (PYSZ) thermal barrier coatings (TBC) on top of NiCoCrAlY bond coatings (BC). To develop this pre-treatment, the influence of the oxygen potential during pre-annealing and pre-oxidation on the life span and failure mechanisms of the entire high temperature coating system upon thermal cycling was investigated. The results of this study showed that the service life of the coating system depended strongly on the composition and microstructure of the thermally grown oxide (TGO) after pre-oxidation. The longer life spans were obtained if the TGO thickened very slowly during thermal cycling due to a large α-Al₂O₃ grain size. Such a slow-growing TGO corresponded with a pre-treatment for which θ-Al₂O₃ was formed during pre-oxidation and for which the yttrium was located within a high density of pegs along the TGO/BC interface after pre-oxidation. If the yttrium was present on top of the TGO after pre-oxidation, a thick mixed alumina-zirconia layer formed upon thermal cycling. This mixed oxide layer contributed significantly to the total oxide layer thickness, resulting in short life spans. The formation of NiAl₂O₄ spinel in between the TBC and the α-Al₂O₃ should be avoided, since this can lead to premature failure along the spinel/α-Al₂O₃ interface.