| 氯盐环境中钢筋的腐蚀原理及防护措施 |
| |
| 引用本文： | 李志勇. 氯盐环境中钢筋的腐蚀原理及防护措施[J]. 山西建筑, 2008, 34(29) |
| |
| 作者姓名： | 李志勇 |
| |
| 作者单位： | 华北电力大学环境科学与工程学院,河北,保定,071003 |
| |
| 摘 要： | 指出钢筋锈蚀是混凝土破坏最重要的原因之一,针对这一情况,研究了钢筋表面的钝化膜及膜的破坏,分析了氯离子的来源及其破坏机理,提出了氯盐侵蚀的防护措施,从而延长混凝土的使用寿命.
|
| 关 键 词： | 钢筋 氯盐 钝化膜 混凝土 |
Corrosion principle of the steel reinforced and protective measures in the chloride environment |
| |
| LI Zhi-yong. Corrosion principle of the steel reinforced and protective measures in the chloride environment[J]. Shanxi Architecture, 2008, 34(29) |
| |
| Authors: | LI Zhi-yong |
| |
| Affiliation: | LI Zhi-yong |
| |
| Abstract: | The author pints out that the steel reinforced corrosion is the most important one reason of the concrete failure,studies the passive film of the reinforcement surface and the failure of the film,analyzes the source and the failure mechanism of the chloride,puts forward the protective measures of the chloride erosion to prolong the service life of the concrete. |
| |
| Keywords: | steel reinforced chloride passive film concrete |