Synthesis of highly crystalline spinel LiMn2O4 by a soft chemical route and its electrochemical performance

Highly crystalline spinel LiMn₂O₄ was successfully synthesized by annealing lithiated MnO₂ at a relative low temperature of 600 °C, in which the lithiated MnO₂ was prepared by chemical lithiation of the electrolytic manganese dioxide (EMD) and LiI. The LiI/MnO₂ ratio and the annealing temperature were optimized to obtain the pure phase LiMn₂O₄. With the LiI/MnO₂ molar ratio of 0.75, and annealing temperature of 600 °C, the resulting compounds showed a high initial discharge capacity of 127 mAh g⁻¹ at a current rate of 40 mAh g⁻¹. Moreover, it exhibited excellent cycling and high rate capability, maintaining 90% of its initial capacity after 100 charge-discharge cycles, at a discharge rate of 5 C, it kept more than 85% of the reversible capacity compared with that of 0.1 C.