Isothermal calorimetry investigation of Li1+xMn2−yAlzO4 spinel

The heat generation of LiMn₂O₄, Li_1.156Mn_1.844O₄, and Li_1.06Mn_1.89Al_0.05O₄ spinel cathode materials in a half-cell system was investigated by isothermal micro-calorimetry (IMC). The heat variations of the Li/LiMn₂O₄ cell during charging were attributed to the LiMn₂O₄ phase transition and order/disorder changes. This heat variation was largely suppressed when the stoichiometric spinel was doped with excess lithium or lithium and aluminum. The calculated entropy change (dE/dT) from the IMC confirmed that the order/disorder change of LiMn₂O₄, which occurs in the middle of the charge, was largely suppressed with lithium or lithium and aluminum doping. The dE/dT values obtained did not agree between the charge and the discharge at room temperature (25 °C), which was attributed to cell self-discharge. This discrepancy was not observed at low temperature (10 °C). Differential scanning calorimeter (DSC) results showed that the fully charged spinel with lithium doping has better thermal stability.