Preparation and properties of some ODS Fe-Cr-Al alloys

Several alloys based on Fe-25Cr-6Al and Fe-25Cr-11Al (wt pct) with additions of yttrium, Al₂O₃, and Y₂O₃ have been prepared by mechanical alloying of elemental, master alloy and oxide powders. The powders were consolidated by extrusion at 1000°C with a reduction ratio of 36:1. The resulting oxide contents were all approximately either 3 vol pct or 8 vol pct of mixed Al₂O₃-Y₂O₃ oxides or of Al₂O₃. The alloys exhibited substantial ductility at 600°C: an alloy containing 3 vol pct oxide could be readily warm worked to sheet without intermediate annealing; an 8 vol pct alloy required intermediate annealing at 1100°C. The 3 vol pct alloys could be recrystallized to produce large elongated grains by isothermal annealing of as-extruded material at 1450°C, but the high temperature strength properties were not improved. However, these alloys, together with some of the 8 vol pct materials, could be more readily recrystallized after rod (or sheet) rolling; sub-stantially improved tensile and stress rupture properties were obtained following 9 pct rod rolling at 620°C and isothermal annealing for 2 h at 1350°C. In this condition, the rup-ture strengths of selected alloys at 1000 and 1100°C were superior to those of competitive nickel-and cobalt-base superalloys. The oxidation resistance of all the alloys was ex-cellent. F. G. WILSON and C. D. DESFORGES, formerly with Fulmer Re-search Institute