Fabrication of NiO Nanoparticle-Coated Lead Zirconate Titanate Powders by the Heterogeneous Precipitation Method

NiO nanoparticle-coated lead zirconate titanate (PZT) powders are successfully fabricated by the heterogeneous precipitation method using PZT, Ni(NO₃)₂·6H₂O, and NH₄HCO₃ as the starting materials. The amorphous NiCO₃·2Ni(OH)₂·2H₂O are uniformly coated on the surface of PZT particles. XRD analysis and the selected-area diffraction (SAD) pattern indicate that the amorphous coating layer is crystallized to NiO after being calcined at 400°C for 2 h. TEM images show that the NiO particles of ∼8 nm are spherical and weakly agglomerated. The thickness of the nanocrystalline NiO coating layer on the surface of PZT particle is ∼30 nm.