Impact of support oxide and Ba loading on the NOx storage properties of Pt/Ba/support catalysts: CO2 and H2O effects

A series of 1 wt.%Pt/_xBa/Support (Support = Al₂O₃, SiO₂, Al₂O₃-5.5 wt.%SiO₂ and Ce_0.7Zr_0.3O₂, x = 5–30 wt.% BaO) catalysts was investigated regarding the influence of the support oxide on Ba properties for the rapid NO_x trapping (100 s). Catalysts were treated at 700 °C under wet oxidizing atmosphere. The nature of the support oxide and the Ba loading influenced the Pt–Ba proximity, the Ba dispersion and then the surface basicity of the catalysts estimated by CO₂-TPD. At high temperature (400 °C) in the absence of CO₂ and H₂O, the NO_x storage capacity increased with the catalyst basicity: Pt/20Ba/Si < Pt/20Ba/Al5.5Si < Pt/10Ba/Al < Pt/5Ba/CeZr < Pt/30Ba/Al5.5Si < Pt/20Ba/Al < Pt/10BaCeZr. Addition of CO₂ decreased catalyst performances. The inhibiting effect of CO₂ on the NO_x uptake increased generally with both the catalyst basicity and the storage temperature. Water negatively affected the NO_x storage capacity, this effect being higher on alumina containing catalysts than on ceria–zirconia samples. When both CO₂ and H₂O were present in the inlet gas, a cumulative effect was observed at low temperatures (200 °C and 300 °C) whereas mainly CO₂ was responsible for the loss of NO_x storage capacity at 400 °C. Finally, under realistic conditions (H₂O and CO₂) the Pt/20Ba/Al5.5Si catalyst showed the best performances for the rapid NO_x uptake in the 200–400 °C temperature range. It resulted mainly from: (i) enhanced dispersions of platinum and barium on the alumina–silica support, (ii) a high Pt–Ba proximity and (iii) a low basicity of the catalyst which limits the CO₂ competition for the storage sites.