STUDY ON IMPACT DAMAGE OF S-GLASS FABRIC REINFORCED LAMINATES

Systematic experimental studies on the sequential damage of centrally transversely impacted plan woven fabric S glass/epoxy laminates have been conducted by using gas gun and penetrant enhanced X ray radiography. The finite element code is developed to understand the stresses distributions in the plates. Based on the study, it can be concluded that the small mass, high velocity impactor can produce more serious damage than large mass, low velocity impactor in the same kinetic energy. The ply orientation has no influence on the force time histories of laminates; with the velocity increasing, the influence of the ply orientation on the damage mode and extent become obvious. Mismatch of ply orientation can deflect the propagation of impact induced cracks.