Photoactivity of anatase–rutile TiO2 nanotubes formed by anodization method

Titania (TiO₂) nanotubes were prepared by anodizing titanium (Ti) foils in an electrochemical bath consisting of 1 M glycerol with 0.5 wt.% NH₄F.The pH of the bath was kept constant at 6 and the anodization voltage was varied from 5 V, 20 V to 30 V. It is found that the morphology of the anodized titanium is a function of anodization voltage with pits-like oxide formed for the sample made at 5 V and samples made at 20 V and 30 V consisted of well-aligned nanotubes growing perpendicularly on the titanium foil. However, the nanotubes formed on the samples made at 30 V were not uniform in terms of the nanotubes' diameter and wall thickness. Regardless of the anodization voltage, as anodised samples were amorphous. The crystal structure evolution was studied as a function of annealing temperatures and was characterised by X-ray diffraction and Raman spectroscopy analyses. Crystallization of the nanotubes to anatase phase occurred at 400 °C while rutile formation occurred at 700 °C. Disintegration of the nanotube arrays was observed at 600 °C and the structure completely vanished at 700 °C. TiO₂ nanotube annealed at 400 °C and containing 100% anatase revealed the highest photocatalytic activity for the degradation of methyl orange. Consequently, these results indicate that diameter, wall thickness, crystal structure and degree of crystallinity of the TiO₂ nanotube arrays are the important factors influencing the efficiency of the photocatalytic activity.