Degradation of Nextel™ 610‐based oxide‐oxide ceramic composites by aluminum oxychloride decomposition products

Nextel? 610 alumina fibers and alumina‐YAG (yttrium‐aluminum garnet) matrices were used to make oxide‐oxide ceramic matrix composites (CMCs) with and without monazite (LaPO₄) fiber‐matrix interfaces. Twelve sequential aluminum oxychloride (AlOCl) infiltrations with 1 hour heat treatments at 1100°C and a final 1 hour heat treatment at 1200°C were used for matrix densification. This matrix processing sequence severely degraded CMC mechanical properties. CMC tensile strengths and interlaminar tensile (ILT) strengths were less than 10 MPa and 1 MPa, respectively. Axial fracture of Nextel? 610 fibers was observed after ILT testing, highlighting the extreme degradation of fiber strength. Extensive characterization was done to attempt to determine the responsible degradation mechanisms. Changes in Nextel? 610 fiber microstructure after CMC processing were characterized by optical microscopy, SEM, and extensively by TEM. In AlOCl degraded fibers, grain boundaries near the fiber surface were wetted with a glass that contained Y₂O₃/SiO₂ or Y₂O₃/La₂O₃/P₂O₅/SiO₂, and near‐surface pores were partially filled with Al₂O₃. This glass must also contain some Al₂O₃ and initially some chlorine. AlOCl decomposition products were predicted using the FactSage^® Thermochemical code, and were characterized by mass spectrometry. Effects of AlOCl precursors on monazite coated and uncoated Nextel? 610 fibers tow and filament strength were evaluated. A mechanism for the severe degradation of the oxide‐oxide CMCs and Nextel? 610 fibers that involves subcritical crack growth promoted by release of chlorine containing species during breakdown of intergranular glasses in an anhydrous environment is proposed.