Effect of processing parameters on structural,morphological and optical Y2O3:Yb3+/Ho3+ powders characteristics

Rod-like and flake-like up-converting Y₂O₃:Yb³⁺/Ho³⁺ particles which are composed of nanoparticles with size less than 100 nm, are prepared by a simple hydrothermal processing at 473 K (3 h) followed by additional thermal treatment at 1373 K (3 and 12 h). The effect of precursor pH value on the formation of Y₂O₃:Yb³⁺/Ho³⁺ is followed through X-ray powder diffractometry (XRPD), scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS). Structural refinement confirms formation of the cubic bixbyte structure (S.G. Ia-3) with the non-uniform accommodation of dopants at C₂ and S₆ cationic sites. Under 978 nm laser excitation, strong green (530–570 nm) up-conversion is observed in all samples. The emission shows a decrease in intensity with an increase in external temperature, indicating FIR (fluorescence intensity ratio) based temperature sensing behavior of 0.52% for the ⁵F₄ → ⁵I₈/⁵S₂ → ⁵I₈ transitions.