| 600 MW机组海水循环泵轮毂腐蚀原因分析 |
| |
| 引用本文： | 杨点中,楼玉民,周江. 600 MW机组海水循环泵轮毂腐蚀原因分析[J]. 华东电力, 2006, 34(11): 74-76 |
| |
| 作者姓名： | 杨点中 楼玉民 周江 |
| |
| 作者单位： | 浙江省电力试验研究院,浙江,杭州,310014;浙江省电力试验研究院,浙江,杭州,310014;浙江省电力试验研究院,浙江,杭州,310014 |
| |
| 摘 要： | 对600MW电站机组海水循环泵轮毂腐蚀进行化学成分分析、金相试验和SEM分析,认为铸造和热处理过程不当是造成海水循环泵轮毂发生早期腐蚀的主要原因.
|
| 关 键 词： | 600 MW机组 海水循环泵轮毂 腐蚀 |
| 文章编号： | 1001-9529(2006)11-0074-03 |
| 修稿时间： | 2006-07-05 |
Corrosion reasons for seawater circulating pump wheel hubs of 600 MW units |
| |
| YANG Dian-zhong,LOU Yu-min,ZHOU Jiang. Corrosion reasons for seawater circulating pump wheel hubs of 600 MW units[J]. East China Electric Power, 2006, 34(11): 74-76 |
| |
| Authors: | YANG Dian-zhong LOU Yu-min ZHOU Jiang |
| |
| Abstract: | After chemical composition analysis,metallography examination,and SEM analysis of corrosion of the seawater circulating pump wheel hub for a 600 MW unit,it is concluded that the corrosion is caused by improper casting and thermal treatment. |
| |
| Keywords: | 600 MW unit seawater circulating pump wheel hub corrosion |