摘    要:开发了一种新型水下湿法自保护药芯焊丝,采用模拟压力舱以及自动焊接系统,在30米模拟水深的条件下进行了焊接试验,焊接结果表明焊接过程稳定,成形良好.按照美国焊接协会水下焊接标准(ANSI/AWS D3.6 1999)对获得的焊接接头的抗拉性能、弯曲性能、硬度以及冲击韧性等进行了研究.拉伸试验试件断裂位置位于母材区,弯曲试验试件弯曲180°没有发生断裂,并无明显裂纹产生,0℃冲击韧性达到30.25J/cm2.研究结果表明,自主研发的水下湿法自保护药芯焊丝可满足CCSE36等级钢的水下30米水深的焊接性能要求.

关 键 词:水下湿法焊接  药芯焊丝  CCSE36钢  力学性能
收稿时间:2013-12-17

Flux-cored wire for underwater wet welding
GUO Ning,WANG Meirong,GUO Wei and FENG Jicai. Flux-cored wire for underwater wet welding[J]. Transactions of The China Welding Institution, 2014, 35(5): 13-16
Authors:GUO Ning  WANG Meirong  GUO Wei  FENG Jicai
Affiliation:1.State Key Laboratory of Advanced Welding and Joining, Harbin Institute of Technology, Harbin 150001, China;Shandong Provincial Key Laboratory of Special Welding Technology, Harbin Institute of Technology at Weihai, Weihai 264209, China2.Shandong Provincial Key Laboratory of Special Welding Technology, Harbin Institute of Technology at Weihai, Weihai 264209, China
Abstract:A novel flux-cored wire for underwater wet welding was developed. The underwater wet welding experiments with the water depth of 30 m were carried out by using a simulated pressure vessel and automatic welding machine. The experimental results show that welding process was stable and the good weld appearance could be obtained. According to the ANSI/AWS D3.6 1999,the tensile strength,bending property,hardness and impact toughness of the joint were studied. The results indicated that the fracture location of tensile test was in base material, no fracture was occurred during bending test and the acceptable impact toughness of joints about 30.25 J/cm2 at 0℃ were also obtained. So the novel flux-cored wire could reach the requirements of underwater wet welding for CCSE36 steel with the water depth of 30 m.
Keywords:underwater wet welding  flux-cored wire  CCSE36 steel  mechanical property