Preparation and photovoltaic properties of anodically grown Ag2O films

The semiconducting and photovoltaic properties of p-type Ag₂O films grown anodically on silver electrodes were studied, in view of possible applications in solar energy conversion. Films were grown in different alkaline solutions; the best results were obtained for 0.02M Ag₂SO₄ + 0.17M NH₄OH + 5.7 × 10^–3M Ba(OH)₂ saturated with Ag₂O powder, stirred mechanically at room temperature. Film thicknesses of up to 10m were thus obtained for the first time in anodically grown Ag₂O. Photovoltaic spectra taken at 300 K give a bandgap ofEg = 1.42 ± 0.04 eV. Evaporated gold on Ag₂O appears to be ohmic while aluminium and platinum are rectifying. The barrier height of Ag/Ag₂O is 0.90 ± 0.02 eV, that of Al/Ag₂O is 0.93 ± 0.02 eV, and that of platinum 0.94 ± 0.02 eV. The best cells give an open-circuit voltage,V_oc, of over 150 mV, and a short circuit current,I_sc = 100A cm^–2 under 50 mW cm^–2 illumination.