| Abstract: | Fluorescence technique was employed for the measurement of the diffusion coefficient of oxygen into polystyrene (PS) latex/modified Na‐activated bentonite (MNaLB) clay composite films. Three different MNaLB content (0, 5, and 20 wt%) composite films were prepared from PS/MNaLB mixtures by annealing them at 200°C, above the glass transition temperature of PS for 10 min. To determine the diffusivity of oxygen in PS/MNaLB composite films, diffusion measurements were performed over the temperature range from 25 to 70°C. Pyrene (P) was used as the fluorescent agent. The diffusion coefficients (D) of oxygen were determined by combining the fluorescence quenching method with Fickian transport model, and were found as a function of temperature for each MNaLB content film. The results showed that D values are strongly dependent on both temperature and clay content in composite film. It was also observed that D coefficients obey Arrhenius behavior, from where diffusion activation energies were measured. POLYM. COMPOS., 2010. © 2009 Society of Plastics Engineers |