Conversion of N2O to N2 on TiO2(1 1 0)

In this study, we examine the interaction of N₂O with TiO₂(1 1 0) in an effort to better understand the conversion of NO_x species to N₂ over TiO₂-based catalysts. The TiO₂(1 1 0) surface was chosen as a model system because this material is commonly used as a support and because oxygen vacancies on this surface are perhaps the best available models for the role of electronic defects in catalysis. Annealing TiO₂(1 1 0) in vacuum at high temperature (above about 800 K) generates oxygen vacancy sites that are associated with reduced surface cations (Ti³⁺ sites) and that are easily quantified using temperature programmed desorption (TPD) of water. Using TPD, X-ray photoelectron spectroscopy (XPS) and electron energy loss spectroscopy (EELS), we found that the majority of N₂O molecules adsorbed at 90 K on TiO₂(1 1 0) are weakly held and desorb from the surface at 130 K. However, a small fraction of the N₂O molecules exposed to TiO₂(1 1 0) at 90 K decompose to N₂ via one of two channels, both of which are vacancy-mediated. One channel occurs at 90 K, and results in N₂ ejection from the surface and vacancy oxidation. We propose that this channel involves N₂O molecules bound at vacancies with the O-end of the molecule in the vacancy. The second channel results from an adsorbed state of N₂O that decomposes at 170 K to liberate N₂ in the gas phase and deposit oxygen adatoms at non-defect Ti⁴⁺ sites. The presence of these O adatoms is clearly evident in subsequent water TPD measurements. We propose that this channel involves N₂O molecules that are bound at vacancies with the N-end of the molecule in the vacancy, which permits the O-end of the molecule to interact with an adjacent Ti⁴⁺ site. The partitioning between these two channels is roughly 1:1 for adsorption at 90 K, but neither is observed to occur for moderate N₂O exposures at temperatures above 200 K. EELS data indicate that vacancies readily transfer charge to N₂O at 90 K, and this charge transfer facilitates N₂O decomposition. Based on these results, it appears that the decomposition of N₂O to N₂ requires trapping of the molecule at vacancies and that the lifetime of the N₂O–vacancy interaction may be key to the conversion of N₂O to N₂.