| 冷轧钢带边鼓缺陷产生原因与控制措施 |
| |
| 引用本文： | 吴玉红,王玉雷,张恒伟,亓振宝.冷轧钢带边鼓缺陷产生原因与控制措施[J].山东冶金,2014(3):18-19. |
| |
| 作者姓名： | 吴玉红 王玉雷 张恒伟 亓振宝 |
| |
| 作者单位： | 山东泰山钢铁集团有限公司,山东莱芜271100 |
| |
| 摘 要： | 分析了冷轧钢带边鼓缺陷的形成机理和产生的原因。通过轧制计划编排、控制轧辊均匀磨损、改善冷轧基板凸度和降低楔形,钢带楔形基本控制在0.04 mm以内,板凸度由平均0.03 mm增加到0.05 mm;冷轧边鼓发生率由0.90%降低到0.30%以内。
|
| 关 键 词： | 冷轧钢带 边鼓 辊缝形状 控制措施 |
Causes and Control Measures of the Ribbing Defect on Cold-Rolled Steel Strips |
| |
| WU Yuhong,WANG Yulei,ZHANG Hengwei,QI Zhenbao.Causes and Control Measures of the Ribbing Defect on Cold-Rolled Steel Strips[J].Shandong Metallurgy,2014(3):18-19. |
| |
| Authors: | WU Yuhong WANG Yulei ZHANG Hengwei QI Zhenbao |
| |
| Affiliation: | (Shandong Taishan Steel Group Corporation, Laiwu 271100, China) |
| |
| Abstract: | The formation mechanism and causes of the ribbing defect on cold-rolled steel strips are analysised in this paper. The wedge of the strip is controlled within 0.04 mm and the crown is increased from 0.03 mm to 0.05 mm by optimizing the arrangement of rolling plan,controlling the uniformity of roll wear,improving the crown of cold rolled base and lowering the wedge; the incidence of ribbing is reduced from 0.90% to 0.30%. |
| |
| Keywords: | cold-rolled steel strip ribbing roll gap shape control measures |