Reciprocating Sliding Friction and Wear Property of Fe3Si Based Alloys Containing Cu in Water Lubrication

Fe₃Si, Fe₃Si alloys containing Cu were fabricated by arc melting followed by hot-pressing. The friction and wear behaviors of Fe₃Si based alloys with and without Cu addition against Si₃N₄ ball in water-lubrication were investigated. The friction coefficient and the wear rates of Fe₃Si based alloys decreased as the load increased. The wear rate of Fe₃Si was higher than that of AISI 304. The addition of Cu can significantly improve the friction and wear properties of Fe₃Si based alloys and substantially reduce the wear rates of Si₃N₄ ball. The wear rate of Fe₃Si–10%Cu was 2.56 × 10⁻⁶ mm³ N⁻¹ m⁻¹ at load of 20 N and decreased to 1.64 × 10⁻⁶ mm³ N⁻¹ m⁻¹ at load of 90 N. The wear rate of Si₃N₄ ball against Fe₃Si–10%Cu was 1.41 × 10⁻⁶ mm³ N⁻¹ m⁻¹, while the wear rate of Si₃N₄ ball against AISI 304 was 5.20 × 10⁻⁶ mm³ N⁻¹ m⁻¹ at load of 90 N. The wear mechanism was dominated by micro-ploughing. The combination of mechanical action (i.e., shear, smear and transference of Cu) and tribochemical reaction of Si₃N₄ with water was responsible for the improved tribological behavior of Fe₃Si alloys containing Cu under high loads.