Corrosion behaviour of bulk ultra-fine grained AZ91D magnesium alloy fabricated by equal-channel angular pressing |
| |
| Authors: | D Song AB Ma JH Jiang PH Lin DH Yang JF Fan |
| |
| Affiliation: | College of Mechanics and Materials, Hohai University, Nanjing 210098, China |
| |
| Abstract: | Effect of microstructure change on corrosion behaviour of equal-channel angular pressed (ECAPed) AZ91D Mg alloy was investigated. The ECAPed alloy with ultra-fine grained (UFG) α-phase matrix and refined β-phase particles displays a significantly lower corrosion resistance, resulting in more pits after in-situ corrosion, higher mass-loss rate immersed in NaCl solution, larger Icorr values in polarization curves and lower fitted Rt values in EIS plots. Two factors weaken the corrosion resistance: the first is the strains-induced crystalline defects providing the α-phase matrix more corrosion activation, the second is the refined β-phase particles losing barrier to the corrosion propagation in α-phase matrix. |
| |
| Keywords: | A Magnesium A Alloy B Polarization B EIS C Pitting corrosion C Effects of strain |
| 本文献已被 ScienceDirect 等数据库收录！ |