Oxidation and interfacial fracture behaviour of NiCrAlY/Al2O3 coatings on an orthorhombic-Ti2AlNb alloy |
| |
Authors: | HQ Li QM Wang SM Jiang J Ma J Gong C Sun |
| |
Affiliation: | State Key Laboratory for Corrosion and Protection, Institute of Metal Research, Chinese Academy of Sciences, 72 Wenhua Road, Shenyang 110016, PR China |
| |
Abstract: | Al2O3 diffusion barriers of various thicknesses have been fabricated by filtered arc ion plating between the NiCrAlY coating and the O-Ti2AlNb alloy. Isothermal oxidation tests and three-point bend tests have been conducted to investigate the influence of the Al2O3 diffusion barriers on the oxidation and interfacial fracture behaviour of the coatings. The results indicate that the Al2O3 diffusion barrier defers interdiffusion and gives oxidation resistance of the NiCrAlY coatings. The thickness of the Al2O3 interlayer not only influences the oxidation behaviour but also affects the interfacial fracture properties. Additionally, thermal exposure affects the critical load in three-point bend tests. |
| |
Keywords: | A Metal coatings A Titanium B SEM C Oxidation C Interfaces |
本文献已被 ScienceDirect 等数据库收录! |