Gamma-radiation-induced corrosion of carbon steel in neutral and mildly basic water at 150 °C

The effect of γ-radiation on the kinetics of carbon steel corrosion has been investigated by characterizing the oxide films formed on steel coupons at 150 °C and at two pH values. Results show that continuous irradiation enhances surface oxide formation with the type of oxide formed dependant on the solution pH. For experiments at 150 °C and a OH⁻] equivalent to that for pH_{25 °C} = 10.6, the surface oxide on carbon steel after γ-irradiation was non-porous and uniform, and no localized corrosion was observed. This oxide, however, appears to be susceptible to brittle fracture during cooling. Raman spectroscopy of the surface film indicates that it is a mixture of the phases of Fe₃O₄ and γ-Fe₂O₃. In contrast, at 150 °C with OH⁻] equivalent to neutral pH_{25 °C}, metal dissolution is significant and the surface oxide film is very porous. Raman spectra show that this oxide film is also composed of a mixture of Fe₃O₄ and γ-Fe₂O_3. The results from this work combined with previously reported electrochemical studies of the same system as a function of pH and temperature can be used to deconvolute the effects of radiation, pH and temperature on the nature of the corrosion process.