Growth of Highly Oriented TlBa2Ca2Cu3O9—y Superconducting Films on Ag Substrates Using a Dip-Coated Barium Calcium Copper Oxide Sol—Gel Precursor

Thin films of Ba_zCa₂Cu₃O₇ a precursor of TIBa₂, Ca₂-Cu₃O_9-y, were prepared by sol-gel synthesis from an all alkoxide solution. The barium and calcium precursors were the respective metals reacted with 2-methoxyethanol, and the copper precursor was copper methoxide complexed by triethanolamine. Silver substrates were coated using the sol-gel solution by dip-coating. Subsequent processing included a low-temperature drying step (600°C), repeated coating to provide the desired thickness, heat treatment at 850°C in oxygen to remove carbon, and reaction at 860°C in a two-zone thallination furnace to produce a TIBa₂Ca₂-Cu₃O_9-y, superconducting film. These films were strongly c-axis-aligned, had a zero-resistance temperature (T₂) of 110 K, and a critical-current density (J_c) of 1.9 × 10₄ A/cmZ at 77 K and zero magnetic field.