| 电流退火对冷轧硅钢组织的影响 |
| |
| 引用本文： | 许光明,孙荣生,李英红. 电流退火对冷轧硅钢组织的影响[J]. 钢铁研究学报, 2008, 20(7): 43-0 |
| |
| 作者姓名： | 许光明 孙荣生 李英红 |
| |
| 作者单位： | 东北大学材料电磁过程研究教育部重点实验室,辽宁,沈阳,110004 |
| |
| 摘 要： | 研究了不同电流条件下退火冷轧无取向硅钢组织的变化规律。结果表明：电流对硅钢组织有显著影响。在施加直流电流退火条件下，再结晶速度比不施加电流退火时快得多，但施加交流电退火时的再结晶速度比施加直流电流退火时慢。
|
| 关 键 词： | 电流退火 硅钢 再结晶 |
| 收稿时间： | 1900-01-01; |
Influence of Current Annealing on Microstructure of Cold-Rolled Si-Steel |
| |
| XU Guang-ming,SUN Rong-sheng,LI Ying-hong. Influence of Current Annealing on Microstructure of Cold-Rolled Si-Steel[J]. Journal of Iron and Steel Research, 2008, 20(7): 43-0 |
| |
| Authors: | XU Guang-ming SUN Rong-sheng LI Ying-hong |
| |
| Affiliation: | Key Laboratory of National Education Ministry for Electromagnetic Processing of Materials, Northeastern University, Shenyang 110004, Liaoning, China |
| |
| Abstract: | The change rule of the microstructure of the cold rolled Si steel annealed under different current was researched. The results show that the current has obvious effect on the microstructure of the Si steel. Under DC condition the nucleation rate of recrystallization is much higher than that without current and is slightly higher than that annealed with AC current. |
| |
| Keywords: | current annealing Si��steel recystallization |