Magnetic and Morphological Properties of Electrodeposited Thick FePt Films on Metallic (Au, Ag, Cu) Underlayers

Electrodeposited thick films of FePt (with the nominal composition 50 % Fe/50 % Pt) on three metallic (Au, Ag, Au) underlayers were annealed at various temperatures. The magnetic and morphological properties of the resulting films were then monitored. The Au and Ag underlayers promoted the growth of the (bct) L1₀ FePt phase. The greater growth of this phase in the films deposited on the Ag underlayer led to the crystallographic texturing in the (001) direction. This was accompanied by a significant magnetic anisotropy and a negative shift of the remanent magnetization in the presence of an applied field. The coercivity of the Ag underlayer films increased to 18 kOe while the coercivity of the Au underlayer films decreased to ～2 kOe when the annealing temperature was increased to 800 ^°C.