Electrochemical effects of silane pretreatments containing cerium nitrate on cathodic disbonding properties of epoxy coated steel |
| |
| Authors: | Sadeq Hooshmand Zaferani Mahmood Peikari Davood Zaarei Iman Danaei |
| |
| Affiliation: | 1. Department of Technical Inspection Engineering , Petroleum University of Technology , Abadan , Iran S-hooshmand@hotmail.com;3. Department of Technical Inspection Engineering , Petroleum University of Technology , Abadan , Iran;4. Technical Faculty , Islamic Azad University , Tehran , Iran |
| |
| Abstract: | In the recent years, silane materials, because of their environmental friendly nature and ease of application have been attended as an alternative for chromate conversion coatings. Different materials were searched for improvement of the efficiency of silane formulation. In this research, pretreatment of carbon steel substrates was carried out using γ-glycidoxypropyl-trimethoxysilane (γ-GPS) as functionalized silane. Cerium nitrate as a corrosion inhibitor material was introduced into the silane material and epoxy resin was applied on the pretreated steel substrates. Effects of the pretreatment on electrochemical properties, cathodic disbondment, dry and wet adhesion strength, and surface morphology of resultant epoxy coating were investigated. Results showed that pretreatment of steel substrate with γ-glycidoxypropyl-trimethoxysilane (γ-GPS) doped with cerium nitrate leads to improvement of cathodic disbondment and also dry and wet adhesion of epoxy coating. Furthermore, this type of pretreatment reduced the disruption of interfacial bonds at the binder/substrate interface. Addition of 2?wt% cerium nitrate into the silane formulation led to the maximum efficiency of resultant coating. |
| |
| Keywords: | adhesives carbon steel cathodic disbondment coating |
|
|