Effect of different air-abrasion protocols on topography,surface wettability and adhesion of MDP monomer-based resin cement to zirconia

This study evaluated the effect of air-abrasion protocols on the topography, surface wettability and adhesion of resin cement to zirconia. Ceramic specimens (N?=?49; n?=?7) (15?mm × 2?mm) were randomly allocated to seven groups to be treated with: (1) Air-abrasion with 45?μm Al₂O₃ (A45), (2) 80?μm Al₂O₃ (A80), (3) 30?μm Al₂O₃ coated with SiO₂ (CoJet) (C30), (4) 30?μm Al₂O₃ coated with SiO₂ (Rocatec Soft) (R30), (5) 110?μm Al₂O₃ coated with SiO₂ (Rocatec Plus) (R110); (6) R110R30 (Rocatec) (R110R30) and (7) control, no conditioning (NC). Air-abrasion was performed using a chairside air-abrasion device (2.5?bar, 10?mm, 90?s). Contact angle measurements were performed using goniometry (n?=?5). MDP-based dual resin cement (Panavia F2.0) was bonded on four locations after air-abrasion protocols (n?=?20 per group). Half of the specimens were tested after 24?h and the other half after thermal cycling (×3000, 5–55?°C). Data were analyzed using 1-, 2-way ANOVA and Tukey’s test (alpha = 0.05). Significantly lower contact angle values were observed for groups C30 (62.6?±?0.91), R30 (61.91?±?1.05) and R110R30 (61.54?±?1.02) compared to those of other groups (65.5?±?0.9–110.61?±?0.9) (p?p?=?0.238). After thermocycling, bond strength results decreased significantly (p?p?