Electrical conductivity changes of bulk tin and Sn-3.0Ag-0.5Cu in bulk and in joints during isothermal aging |
| |
Authors: | Bin Liu Fu Guo |
| |
Affiliation: | Bin Liu~(1,2)) and Fu Guo~(2)) 1) Institute of Building Environment and Energy Efficiency,China Academy of Building Research,Beijing 100044,China 2) College of Materials Science and Engineering,Beijing University of Technology,Beijing 100124,China |
| |
Abstract: | The changes of electrical conductivity(resistance)between Sn-3.0Ag-0.5Cu solder joints and printed circuit board(PCB)assembly during aging at 125℃ were investigated by the four-point probe technique.The microstructural characterizations of interfacial layers between the solder matrix and the substrate were examined by optical microscopy and scanning electronic microscopy.Different types of specimens were designed to consider several factors.The experimental results indicate that electrical conductivities(resistances)and residual shear strengths of the solder joint specimens significantly decrease after 1000 h during isothermal aging.Microcracks generate in the solder matrix at the first 250 h.Besides,the evolutions of microstructural characterizations at the interface and the matrix of solder joints were noted in this research. |
| |
Keywords: | lead-free solder electrical conductivity isothermal aging,microcrack thermal stress |
本文献已被 CNKI 维普 万方数据 等数据库收录! |
|