Characterisation by TPR, XRD and NOx Storage Capacity Measurements of the Ageing by Thermal Treatment and SO2 Poisoning of a Pt/Ba/Al NOx-Trap Model Catalyst

The deactivation of a Pt/Ba/Al₂O₃ NO _x -trap model catalyst submitted to SO₂ treatment and/or thermal ageing at 800 °C was studied by H₂ temperature programmed reduction (TPR), X-ray diffraction (XRD) and NO _x storage capacity measurements.The X-ray diffractogram of the fresh sample exhibits peaks characteristic for barium carbonate. Thermal ageing leads to the decomposition of barium carbonate and to the formation of BaAl₂O₄. The TPR profile of the sulphated sample shows the presence of (i) surface aluminium sulphates, (ii) surface barium sulphates, (iii) bulk barium sulphates. The exposure to SO₂ after ageing leads to a small decrease of the surface barium-based sulphates, expected mainly as aluminate barium sulphates. This evolution can be attributed to a sintering of the storage material. TPR experiments also show that thermal treatment at 800 °C after the exposure to SO₂ involves the decomposition of aluminium surface sulphates to give mainly bulk barium sulphates, also pointed out by XRD. Thus, the thermal treatment at 800 °C leads to a stabilization of the sulphates.These results are in accordance with the NO _x storage capacity measurements. On non-sulphated catalysts, the treatment at 800 °C induces to a decrease of the NO _x storage capacity, showing that barium aluminate presents a lower NO _x storage capacity than barium carbonate. Sulphation strongly decreases the NO _x storage capacity of catalysts, whatever the initial thermal treatment, showing that barium sulphates inhibit the NO₂ adsorption. Moreover, the platinum activity for the NO to NO₂ oxidation is lowered by thermal treatments.