Low Breakdown Voltage Varistors by Grain Boundary Diffusion of Molten Bi2O3 in ZnO

Diffusion of molten Bi₂O₃ into the grain boundaries of sintered, alumina-doped (0.23 and 0.7 mol%) ZnO pellets resulted in varistors with breakdown voltages in the 3–5 V range and nonlinearity coefficients of 10–24. The varistors were fabricated by spreading a thin layer of Bi₂O₃ powder on the surface of ZnO pellets and heating the combination to various temperatures (860–1155°C) and different times. The highest nonlinearity coefficients (20–24) and lowest breakdown voltages (3–5 V) were recorded in samples annealed at 860°C for 35 min. Longer annealing times and/or higher temperatures resulted in progressively higher breakdown voltages. Eventually the devices became insulating, which was attributed to the formation of an insulating Bi₂O₃ layer between the grains. Separate wetting experiments have shown that the penetration of Bi₂O₃ into ZnO grain boundaries was a strong function of alumina doping —the penetration rate was decreased by a factor of 5–7 as the ZnO was doped with as little as 0.2 mol% alumina. It is this slowing down of the penetration of the ZnO grain boundaries that is believed to be critical in the development of the low breakdown voltages observed.