Preparation and Properties of Glass-Ceramics Derived from Nitrogen-Containing β-Spodumene Glasses

Crystallization of Li-Al-Si-O-N oxynitride glasses based on the β-spodumene composition and the properties of the resultant glass-ceramics have been studied. The onset of the precipitation of metastable high-quartz solid solution and its transformation to β-spodumene shift to higher temperatures with increasing nitrogen content of the oxynitride glasses. Nitrided glass-ceramics crystallized at 1200°C have negative thermal expansion coefficients, since high-quartz structure is maintained up to 1000° and 1200°C. Knoop hardness and density of the glass-ceramics increase with increasing nitrogen content. There was evidence that part of the nitrogen atoms were incorporated into the high-quartz solid-solution structure and that a small amount of the minor phase of Si₂N₂O was precipitated in highly nitrided glass-ceramics.