Dispersion and reaction of TiB2 in liquid iron alloys

Abstract

The degree of reaction and dispersion achieved when TiB₂ powders are melted in contact with liquid iron based alloys has been assessed via a levitation dispersion test which had been developed earlier. Both Fe₂B and TiC were observed to form as a result of dissolution and reaction of TiB₂. The formation of TiC occurs during the reaction of commercial grade TiB₂ with liquid iron alloys containing as little as 0·08 wt-%C. The reaction of high purity TiB₂ with liquid iron alloys containing 0·24 wt-%C does not however lead to TiC formation. The formation of Fe₂B was observed for all conditions tested, owing to the effectively zero solubility of boron in solid iron. The TiB₂ remaining after dissolution and reaction was found to produce relatively good dispersions in the iron matrix and therefore additions of TiB₂ to liquid iron alloys may provide a means of producing Fe–TiB₂ composite materials. However, the brittle properties of Fe₂B will mean that, whereas such materials may be very hard, they are likely to lack toughness.

MST/1477