A7N01铝合金焊接接头的疲劳特性及寿命预测(英文)

研究A7N01铝合金焊接接头的疲劳特性,提出基于疲劳裂纹萌生寿命的寿命预测模型。母材、热影响区和焊缝三个区域内的疲劳裂纹萌生寿命差异较小。在这三个区域内,疲劳裂纹萌生寿命与疲劳总寿命之比是一个依赖于材料的参数,对于母材、热影响区和焊缝分别为26.32%、40.21%和60.67%。提出的疲劳寿命预测模型与实验结果和Basquin’s模型预测结果吻合良好。利用扫描电子显微镜(SEM)对疲劳断口进行观察,发现焊缝区域的裂纹萌生于焊接过程中产生的光滑表面。热影响区内疲劳裂纹萌生于熔合区气孔。母材中破碎的第二相是引起疲劳裂纹的主要原因。

Fatigue behavior and life prediction of A7N01 aluminium alloy welded joint

Fatigue characteristics of A7N01 aluminium alloy welded joint were investigated and a fatigue crack initiation life-based model was proposed. The difference of fatigue crack initiation life among base metal, weld metal and heat affected zone (HAZ) is slight. Furthermore, the ratio of fatigue crack initiation life (Ni) to fatigue life to failure(Nf) is a material dependent parameter, 26.32%, 40.21% and 60.67% for base metal, HAZ and weld metal, respectively. Total fatigue life predicted using the presented model is in good agreement with the experimental data and that using Basquin’s model. The observation results of fatigue fracture surfaces, using scanning electron microscope (SEM), demonstrate that fatigue crack initiates from smooth surface due to welding process for weld metal, blowhole in HAZ causes fatigue crack initiation, and the crushed second phase particles play an important part in fatigue crack initiation in base metal.