Friction Stir Weldabilities of AA1050-H24 and AA6061-T6 Aluminum Alloys |
| |
Authors: | Huijie LIU Hidetoshi FUJII Masakatsu MAEDA Kiyoshi NOGI |
| |
Affiliation: | National Key Laboratory of Advanced Welding Production Technology, Harbin Institute of Technology, Harbin 150001, China... |
| |
Abstract: | The friction stir weldabilities of the strain-hardened AA1050-H24 and precipitate-hardened AA6061-T6 aluminum alloys were examined to reveal the effects of material properties on the friction stir welding behavior. The experimental results are obtlained. (1) For AA1050-H24, the weld can possess smoother surface ripples; there is no elliptical weld nugget in the weld; there is no discernible interface between the stir zone and the thermomechanically affected zone;and the internal defect of the weld looks like a long crack and is located in the lower part of the weld. (2) For AA6061-T6, the weld usually possesses slightly rougher surface ripples; an elliptical weld nugget clearly exists in the weld; there are discernible interfaces among the weld nugget, thermomechanically affected zone and heat affected zone; and the internal defect of the weld is similar to that of the AA1050-H24 weld. (3) The effective range of welding parameters for AA1050-H24 is narrow, while the one for AA6061-T6 is very wide. (4) The maximum tensile strength efficiency of the AA1050-H24 joints is similar to that of the AA6061-T6 joints, i.e. 79% and 77%, respectively. |
| |
Keywords: | Friction stir weldability Aluminum alloy Welding parameter Mechanical properties |
本文献已被 CNKI 万方数据 等数据库收录! |
| 点击此处可从《材料科学技术学报》浏览原始摘要信息 |
|
点击此处可从《材料科学技术学报》下载全文 |
|