800MPa高强钢的焊接性试验研究
引用本文:杨莉,郑军,黄小婷.800MPa高强钢的焊接性试验研究[J].中原工学院学报,1999(2).
作者姓名:杨莉  郑军  黄小婷
作者单位:郑州纺织工学院机械系,郑州水工机械厂
摘    要:采用热影响区最高硬度试验、斜Y型坡口裂纹试验及焊接线能量的测试等手段研究了板厚分别为20mm及42mm的800MPa高强钢的焊接性。结果表明:只要采用合适的预热温度及焊接线能量就可得到高质量的焊接接头。建议工程上采用的焊接线能量为:板厚20mm,E<30kJ/cm;板厚42mm,E<45kJ/cm

关 键 词:高强钢  800MPa  焊接性

Study on the Weldability of 800 MPa High Strength Steel
YANG Li,ZHENG Jun,HUANG Xiaoting.Study on the Weldability of 800 MPa High Strength Steel[J].Journal of Zhongyuan Institute of Technology,1999(2).
Authors:YANG Li  ZHENG Jun  HUANG Xiaoting
Abstract:The weldability of 800 MPa high strength steel has been studied with 20 mm and 42 mm thickness plates by the maximum hardness test of heat-affected zone,Y slit cracking test and the test of weld energy input etc. The result shows that the high quality welded joint can be got by using appropriate preheat temperature and weld energy input.The weld energy input is suggested to be used in project as follows:20 mm thick, E<30 kJ/cm; 42 mm thick, E<45 kJ/cm.
Keywords:high strength steel  800 MPa  weldability  