Corrosion mechanisms of Al2O3/MgAl2O4 by V2O5, NiO, Fe2O3 and vanadium slag

The effects of V₂O₅, NiO, Fe₂O₃ and vanadium slag on the corrosion of Al₂O₃ and MgAl₂O₄ have been investigated. The specimens of Al₂O₃ and MgAl₂O₄ with the respective oxides above mentioned were heated at 10 °C/min from room temperature up to three different temperatures: 1400, 1450 and 1500 °C. The corrosion mechanisms of each system were followed by XRD and SEM analyses. The results obtained showed that Al₂O₃ was less affected by the studied oxides than MgAl₂O₄. Alumina was only attacked by NiO forming NiAl₂O₄ spinel, while the MgAl₂O₄ spinel was attacked by V₂O₅ forming MgV₂O₆. It was also observed that Fe₂O₃ and Mg, Ni, V and Fe present in the vanadium slag diffused into Al₂O₃. On the other hand, the Fe₂O₃ and Ca, S, Si, Na, Mg, V and Fe diffused into the MgAl₂O₄ structure. Finally, the results obtained were compared with those predicted by the FactSage software.