Dielectric and ferroelectric properties of Ba0.8Sr0.2Ti1−5x/4NbxO3 ceramics

Ba_0.8Sr_0.2Ti_1−5x/4Nb_xO₃ ceramics, x = 0, 0.01, 0.05, 0.10, were fabricated by conventional solid-state reaction. With increasing niobium content the ferroelectric phase transition temperature decreases linearly, and the dispersivity of the transition increases. Niobium B-site decreases transition temperature more pronounced than Sr²⁺ at A-site. The heterovalent substitution of Nb⁵⁺ in low content causes local defect dipole, while more substitutions introduce disorder to disturb the long-range dipole correlation. Ba_0.8Sr_0.2Ti_1−0.5/4Nb_0.1O₃ ceramic shows weak ferroelectric loop at room temperature far from its transition temperature, 153 K.