Rapid isothermal annealing of high- and low-energy ion-implantedInP and In0.53Ga0.47As

Rapid isothermal annealing (RIA) was performed on 0.5-16-MeV Si ⁺, 1-MeV Be⁺, and 150-keV Ge⁺ implanted InP:Fe and 380-keV Fe⁺ implanted InGaAs. Annealings were performed in the temperature range 800-925°C using an InP proximity wafer in addition to the Si₃N₄ dielectric cap. Dopant activations close to 100% were obtained for 3×10¹⁴ cm^-2 Si⁺ and 2×10¹⁴ cm^-2 Be⁺ implants in InP:Fe. For the elevated temperature (200°C) 1×10¹⁴ cm^-2 Ge⁺ implant, a maximum of 50% activation was obtained. No redistribution of dopant was observed for Si and Ge implants due to annealing. However, redistribution of dopant was seen for Be and Fe implants due to annealing. Phosphorous coimplantation has helped to eliminate the Be in-diffusion problem in InP, but did not help to reduce Fe in-diffusion and redistribution in InGaAs. Using an RIA cycle with low temperature and short duration is the only solution to minimize Fe redistribution in InGaAs