Measurement of Gibbs energies of formation of CoF2 and MnF2 using a new composite dispersed solid electrolyte

Gibbs energies of formation of CoF₂ and MnF₂ have been measured in the temperature range from 700 to 1100 K using Al₂O₃-dispersed CaF₂ solid electrolyte and Ni+NiF₂ as the reference electrode. The dispersed solid electrolyte has higher conductivity than pure CaF₂ thus permitting accurate measurements at lower temperatures. However, to prevent reaction between Al₂O₃ in the solid electrolyte and NiF₂ (or CoF₂) at the electrode, the dispersed solid electrolyte was coated with pure CaF₂, thus creating a composite structure. The free energies of formation of CoF₂ and MnF₂ are (± 1700) J mol⁻¹; {fx37-1} The third law analysis gives the enthalpy of formation of solid CoF₂ as ΔH° (298·15 K) = −672·69 (± 0·1) kJ mol⁻¹, which compares with a value of −671·5 (± 4) kJ mol⁻¹ given in Janaf tables. For solid MnF₂, ΔH°(298·15 K) = − 854·97 (± 0·13) kJ mol⁻¹, which is significantly different from a value of −803·3 kJ mol⁻¹ given in the compilation by Barinet al.