α'相形成与铁铬铝合金的脆性
引用本文:杜国维, 蔡家敏, 章小雁. α'相形成与铁铬铝合金的脆性[J]. 工程科学学报, 1989, 11(1): 63-68. DOI: 10.13374/j.issn1001-053x.1989.01.012
作者姓名:杜国维  蔡家敏  章小雁
摘    要:应用电子显微镜、X射线衍射技术,对低温长期使用的铁铬铝电热合金进行分析。结果表明:晶粒长大以及铬原子含量为75%左右的铁铬二元α'相在晶界和基体中析出,是导致合金变脆的主要原因;通常微量碳化物Cr23C6相以及σ相总是沿晶界分布。

关 键 词:铁铬铝合金  电热合金  晶粒平均直径  断裂
收稿时间:1986-04-25

a' Phase Formation and Embrittlement of Fe-Cr-Al Alloy
Du Guowei, Cai Jiamin, Zhang Xiaoyan. a' Phase Formation and Embrittlement of Fe-Cr-Al Alloy[J]. Chinese Journal of Engineering, 1989, 11(1): 63-68. DOI: 10.13374/j.issn1001-053x.1989.01.012
Authors:Du Guowei  Cai Jiamin  Zhang Xiaoyan
Abstract:Using electron microscopy and X-ray diffraction techniques, the structure changes of Fe-Cr-Al alloy being used at low temperature for a long time were investigated. The results demonstrated that increase in embri-ttlement for the alloy was mainly caused by grain growth and α'-phase precipitation which contained 75 at% Cr; as usual, Small amount σ-phase and carbide Gr23C6 precipitated at grain boundaries.
Keywords:Fe-Cr-Al alloy  electro-heating alloy  embrittlement  fracture