Torsional braid analysis of the aromatic amine cure of epoxy resins

The cure behavior of diglycidyl ether of bisphenol A (DGEBA) type of epoxy resins with three aromatic diamines, 4,4′-diaminodiphenyl methane (DDM), 4,4′-diaminodiphenyl sulfone (44DDS), and 3,3′-diaminodiphenyl sulfone (33DDS) was studied by torsional braid analysis. For each curing agent the stoichiometry of the resin mixtures was varied from a two to one excess of amino hydrogens per epoxy group to a two to one excess of epoxy groups per amino hydrogen. Isothermal cures of the resin mixtures were carried out from 70 to 210°C (range depending on epoxy—amine mixture), followed by a temperature scan to determine the glass transition temperature (T_g). The times to the isothermal liquid-to-rubber transition were shortest for the DDM mixtures and longest for the 44DDS mixtures. The liquid-to-rubber transition times were also shortest for the amine excess mixtures when stoichiometry was varied. A relatively rapid reaction to the liquid-to-rubber transition was observed for the epoxy excess mixtures, followed by an exceedingly slow reaction process at cure temperatures well above the T_g. This slow process was only observed for epoxy excess mixtures and eventually led to significant increases in T_g. Using time—temperature shifts of the glass transition temperature vs. logarithm of time, activation energies approximately 50% higher were derived for this process compared to those derived from the liquid-to-rubber transition. The rate of this reaction was virtually independent of curing agent and was attributed to etherification taking place in the epoxy excess mixtures. © 1994 John Wiley & Sons, Inc.