Fracture of notched polycarbonate under hydrostatic pressure |
| |
Authors: | M Ishikawa I Narisawa |
| |
Affiliation: | (1) Department of Fiber and Polymer Engineering, Faculty of Engineering, Yamagata University, 992 Yonezawa, Japan |
| |
Abstract: | The brittle fracture behaviour and plastic deformation of round-notched polycarbonate bars subjected to three-point bending under hydrostatic pressure have been studied. Below a certain critical pressure, the brittle fracture initiated from an internal craze nucleated at the tip of the local plastic zone ahead of the notch rooT. The position of the nucleation of the craze receded from the tip of the notch with increasing applied pressure. When the pressure was increased over a critical value, general yielding occurred by passage of the plastic zone across the notched cross-section, that is, the brittle to ductile transition took place. A qualitative analysis of the stress distribution within the plastic zone explains that the brittle to ductile transition under hydrostatic pressure occurs when the general yield takes place before a critical stress for brittle crack propagation is reached. |
| |
Keywords: | |
本文献已被 SpringerLink 等数据库收录! |
|