Ultrasonic dissolution of brazing of 55% SiCp/A356 composites |
| |
Authors: | ZHANG Yang YAN Jiu-chun CHEN Xiao-guang CUI Yan |
| |
Affiliation: | ZHANG Yang,YAN Jiu-chun,CHEN Xiao-guang,CUI Yan State Key Laboratory of Advanced Welding Production Technology,Harbin Institute of Technology,Harbin 150001,China |
| |
Abstract: | The brazing of 55% SiCp/A356 (volume fraction) composites in air using Zn-Al alloy as a filler metal was investigated. During the brazing process, ultrasonic vibrations were applied to samples for bonding and a significant dissolution of the filler metal into the matrix alloy in the base materials occurred. As brazing temperatures were increased, the thickness of the partial melting layers in the base material increased. SiC particles in the partial melting layer of the base material were transferred into the liquid filler under ultrasonic action and a bond with homogeneously distributed reinforcements was obtained after solidification. The volume fraction of SiC particles in the bonds could be varied by changing the brazing temperature. The maximum SiC particle volume fraction of the bond material reached 37% at a brazing temperature of 500 ℃. The shear strength of the brazed bonds was improved at pressures up to 244 MPa (at 20 ℃) and increased by 133.8% (at 200 ℃) compared with the filler of the Zn-based alloy. |
| |
Keywords: | aluminum matrix composites brazing ultrasonic dissolution of brazing composite bond |
本文献已被 CNKI 万方数据 ScienceDirect 等数据库收录! |