Water vapor sensitivity of nanosized La(Co, Mn, Fe)1−x(Cu, Pd)xO3 perovskites during NO reduction by C3H6 in the presence of oxygen

A series of La(Co, Mn, Fe)_1?x(Cu, Pd)_xO₃ perovskites having high specific surface areas and nanosized crystal domains was prepared by reactive grinding. The solids were characterized by N₂ adsorption, X-ray diffraction (XRD), scanning electron microscopy (SEM), temperature programmed desorption (TPD) of O₂, NO + O₂, C₃H₆, in the absence or presence of 5% H₂O, Fourier transform infrared (FTIR) spectroscopy, as well as activity tests towards NO reduction by propene under the conditions of 3000 ppm NO, 3000 ppm C₃H₆, 1% O₂, 0 or 10% H₂O, and 50,000 h^?1 space velocity. The objective was to investigate the influence of H₂O addition on catalytic behavior. A good performance (100% NO conversion, 77% N₂ yield, and 90% C₃H₆ conversion) was achieved at 600 °C over LaFe_0.8Cu_0.2O₃ under a dry feed stream. With the exposure of LaFe_0.8Cu_0.2O₃ to a humid atmosphere containing 10% water vapor, the catalytic activity was slightly decreased yielding 91% NO conversion, 51% N₂ yield, and 86% C₃H₆ conversion. A competitive adsorption between H₂O vapor with O₂ and NO molecules at anion vacancies over LaFe_0.8Cu_0.2O₃ was found by means of TPD studies here. A deactivation mechanism was therefore proposed involving the occupation of available active sites by water vapor, resulting in an inhibition of catalytic activity in C₃H₆ + NO + O₂ reaction. This H₂O deactivation was also verified to be strictly reversible by removing steam from the feed.